Synthesis, characterization, and biological properties of composites of hydroxyapatite and hexagonal boron nitride
Küçük Resim Yok
Tarih
2018
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Wiley
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Hydroxyapatite (HA), obtained from bovine bones, was successfully reinforced with hexagonal boron nitrite (h-BN). h-BN/HA composites, with BN content up to 1.5 wt %, were sintered at various temperatures between 1000 and 1300 degrees C, in air. Well-sintered samples were obtained after sintering at 1200 and 1300 degrees C. The presence of h-BN contributed to dense, fine, and well-crystallized microstructure. The results of X-ray diffraction analysis and FT-IR spectroscopy showed that the produced composites comprised biphasic beta-TCP/HCA (HCA: carbonate partially substituted HA). High values of mechanical properties were achieved, namely compression strength 155 MPa for the sample 0.5% h-BN/HA and Vickers microhardness of 716 HV for the samples 1.5% h-BN/HA, both sintered at 1300 degrees C. U2OS human bone osteosarcoma proliferation and cell viability showed no adverse effect in the presence of h-BN/HA, suggesting the potential use of the produced materials as safe biomaterials in bone tissue engineering. (C) 2017 Wiley Periodicals, Inc.
Açıklama
Anahtar Kelimeler
Composites, Hydroxyapatite, Bovine Bone, Hexagonal Boron Nitride, Bioceramic, Mechanical-Properties, Sintering Temperature, Apatite, Nanoparticles, Nanotubes, Bha
Kaynak
Journal of Biomedical Materials Research Part B-Applied Biomaterials
WoS Q Değeri
Q2
Scopus Q Değeri
Q2
Cilt
106
Sayı
6